E.P. Chen & George C. Sih 
Cracks in composite materials [PDF ebook] 
A compilation of stress solutions for composite systems with cracks

Ajutor

Composites offer great promise as light weight and strong materials for high performance structures. One of the major advantages of these materials as compared with metals is the basic way in which heterogeneity resist crack extension. In a fiber/matrix composite system, the fibers tend to cause cracks to form at closer spacing and delay the formation of a large crack. The enhancement of local failure such as fiber breaking, matrix cracking and interface debonding further reduces the energy level which might have otherwise reached the point of catastrophic failure. Even though substantial tests have been made on composite materials, little has been gained in the understanding and development of a predic- tive procedure for composite failure. There are fundamental difficulties associated with incorporating the nonhomogeneous and anisotropic prop- erties of the composite into the continuum mechanics analysis. Additional uncertainties arise from voids and defects that are introduced in the composite during manufacturing. Even a small quantity of mechanical imperfections can cause a marked influence on the composite strength. Moreover, the interface properties between the fibers and matrix or bonded laminae can also affect the load transmission characteristics significantly. It would be impossible to establish predictive procedures for composite failure unless realistic guidelines could be developed to control the manufacturing quality of composite systems.

€321.42
Metode de plata
Cumpărați această carte electronică și primiți încă 1 GRATUIT!
Limba Engleză ● Format PDF ● ISBN 9789400983403 ● Editura Springer Netherlands ● Publicat 2012 ● Descărcabil 3 ori ● Valută EUR ● ID 4716894 ● Protecție împotriva copiilor Adobe DRM
Necesită un cititor de ebook capabil de DRM

Mai multe cărți electronice de la același autor (i) / Editor

36.596 Ebooks din această categorie